Renewable Design for Shielded Flux Cored Welding Wire - E81T1-B2C Low Alloy Steel Flux Cored Wire – Yichen

E81T1-B2C

E81T1-B2C Low Alloy Steel Flux Cored Wire

The E81T1-B2C low alloy steel flux cored wire involves the utilization of Titanium slag system. Thisgas shielded welding wire is well-suited for 1%Cr-0.5%Mo heat resistant steel. Excellent weldability and stable arc can be achieved in all welding positions while offering low spatter, flawless bead appearance and superior slag detachability.

This kind of low alloy steel flux cored wire requires preheat process. The working temperature of this welding consumable is lower than 520℃ Therefore, our heat resistant steel flux cored wire is highly recommended for low alloy steel such as 15CrMo applicable for boiler, pressure vessel, oil tanker and oil refining equipment, etc.

Standards
GB/T 17493-2008 E551T1-B2C
AWS A5.29 E81T1-B2C

Chemical composition of deposited metal (%)

C Mn Si P S Cr Mo
Standard 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.00-1.50 0.40-0.65
Typical 0.06 0.79 0.19 0.011 0.008 1.20 0.45

Mechanical properties of deposited metal (620℃ × 1h)

Rm (MPa) Rp0.2 (MPa) A5 (%)
Standard 550-690 ≥470 ≥19
Typical 630 560 22

Recommended welding data (DC+, shielding gas: CO2)

Wire diameter (mm) Current (A) Voltage (V) Gas (l/min)
Φ1.2 200-280 24-30 15-20
Φ1.6 220-300 24-32 15-20

  • Renewable Design for Shielded Flux Cored Welding Wire - E81T1-B2C Low Alloy Steel Flux Cored Wire – Yichen Related Video: