E91T5-B3C Low Alloy Steel Flux Cored Wire

2

E91T5-B3C Low Alloy Steel Flux Cored Wire

The E91T5-B3C low alloy steel flux cored wire is formulated with basic type slag system. This low hydrogen welding wire shows remarkable resilience to heat and oxidation. The excellent wedability and mechanical properties of this CO2 welding wire is responsible for stable arc, low spatter and impressive formation.

This low alloy steel flux cored wire requires 300℃ preheat for perfect welds. The heat resistant steel wire is widely applied to low alloy steel structures such as 2.5Cr-1Mo used in high-temperature high-pressure pipeline, chemical machinery and petroleum cracking equipment, etc.

Standards
GB/T17493-2008 E620T1-B3C
AWS A5.29 E90T5-B3C

Chemical composition of deposited metal (%)

C Mn Si Cr Mo S P
Standard ≤0.12 ≤1.25 ≤0.80 2.00-2.50 0.90-1.20 ≤0.03 ≤0.03
Typical 0.07 0.60 0.15 2.08 0.93 0.017 0.012

Mechanical properties of deposited metal(690℃ × 1h)

Rm (MPa) Rp0.2 (MPa) A5 (%)
Standard 620-760 ≥540 ≥17
Typical 680 595 22

Recommended welding data (DC+, shielding gas: CO2)

Wire diameter (mm) Current (A) Voltage (V) Gas (l/min)
Φ1.2 200-260 24-30 15-20
Φ1.6 220-300 24-32 15-20

E91T5-B3C Low Alloy Steel Flux Cored Wire Related Video: