E81T5-B2VC Low Alloy Steel Flux Cored Wire

12

E81T5-B2VC Low Alloy Steel Flux Cored Wire

The E81T5-B2VC low alloy steel flux cored wire is formulated with basic type slag system. This CO2 welding wire requires 200-300℃preheat for perfect welds. Moreover, this flux cored wire model generates stable arc, low spatter and absorbing finish.

This gas shielded wire remains excellent weldability and mechanical properties in welding of low alloy steel such as 12CrMoV at temperature lower than 540℃

Standards
GB/T17493-1998 E550T5-B2V
AWS A5.29 E81T5-B2VC

Chemical composition of deposited metal (%)

C Mn Si Cr Mo S P V
Standard 0.05-0.12 ≤1.25 ≤0.80 1.00-1.50 0.40-0.65 ≤0.030 ≤0.030 0.10-0.35
Typical 0.07 0.79 0.26 1.08 0.43 0.009 0.011 0.19

Mechanical properties of deposited metal (690℃ × 2h)

Rm (MPa) Rp0.2 (MPa) A5 (%)
Standard 550-690 ≥470 ≥19
Typical 618 535 22

Recommended welding data (DC+, shielding gas: CO2)

Wire diameter (mm) Current (A) Voltage (V) Gas (l/min)
Φ1.2 200-260 24-30 15-20
Φ1.6 220-300 24-32 15-20